Shape: | Round |
---|
SAE J525 Welded cold draw low carbon steel tubing annealed for bending and flaring
Size range: O.D.:6-350mm W.T.:1-15mm L: According to customer Order
Applications: for Bending and Flaring to auto parts
Auto motive tubing with various material
Table 1- TUBING OUTSIDE DIAMATER TOLERANCE | |||||||
Nominal Tubing OD mm |
Tolerance OD ±mm |
Tolerance ID ±mm |
|||||
Up to 9.50 | 0.05 | 0.05 | |||||
Over 9.50 to 15.88 inclusive | 0.06 | 0.06 | |||||
Over 15.88 to 50.80 inclusive | 0.08 | 0.08 | |||||
Over 50.8 to 63.50 inclusive | 0.10 | 0.10 | |||||
Over 63.50 to 76.20 inclusive | 0.13 | 0.13 | |||||
Over 76.20 to 100.00 inclusive | 0.15 | 0.15 | |||||
WT tolerance shall be not more than 10% |
Table 2- TUBING WALL THICKNESS TOLERANCE | |||||||
Nominal Wall Thickness |
Nominal OD Through 22mm ±mm |
Nominal OD 22-48mm ±mm |
Nominal OD 48-100mm ±mm |
||||
0.89 | 0.05/0.05 | 0.05/0.05 | 0.05/0.05 | ||||
1.00 | 0.05/0.05 | 0.05/0.08 | 0.05/0.08 | ||||
1.25 | 0.05/0.05 | 0.05/0.08 | 0.05/0.08 | ||||
1.50 | 0.05/0.05 | 0.05/0.08 | 0.05/0.08 | ||||
1.65 | 0.05/0.05 | 0.05/0.08 | 0.05/0.08 | ||||
2.00 | 0.05/0.05 | 0.05/0.08 | 0.05/0.08 | ||||
2.11 | 0.05/0.05 | 0.05/0.08 | 0.05/0.08 | ||||
2.410 | 0.05/0.05 | 0.05/0.08 | 0.08/0.08 | ||||
2.500 | 0.05/0.08 | 0.05/0.10 | 0.08/0.08 | ||||
2.770 | 0.05/0.08 | 0.05/0.10 | 0.08/0.08 | ||||
3.000 | 0.05/0.08 | 0.05/0.10 | 0.08/0.08 | ||||
3.050 | 0.05/0.08 | 0.05/0.10 | 0.08/0.08 | ||||
3.40 | - | 0.05/0.10 | 0.08/0.08 | ||||
3.75 | - | 0.05/0.10 | 0.08/0.08 | ||||
4.00 | - | 0.08/0.10 | 0.08/0.10 | ||||
4.19 | - | 0.08/0.10 | 0.08/0.10 | ||||
4.57 | - | 0.10/0.10 | 0.08/0.13 | ||||
5.00 | - | 0.10/0.13 | 0.10/0.13 | ||||
Table 2- CHEMICAL REQUIREMENTS | |||||||
Element | % | ||||||
Carbon | 0.06-0.18 | ||||||
Manganese | 0.30 to 0.60 | ||||||
Phosphpris | 0.040 max | ||||||
Sulfur | 0.050 max | ||||||
Table 3- MECHANICAL PROPERTIES | |||||||
Properties | Value | ||||||
Yield Strength,min | 170 Mpa | ||||||
Ultimate Strenth,min | 310 Mpa | ||||||
Elongation in 50mm, min | 35% | ||||||
Hardness ( Rockwell B),max | 65.00 |